ref: -0 tags: reactive oxygen accelerated aging neural implants date: 10-07-2015 18:45 gmt revision:1 [0] [head]

PMID-25627426 Rapid evaluation of the durability of cortical neural implants using accelerated aging with reactive oxygen species.

  • Takmakov P1, Ruda K, Scott Phillips K, Isayeva IS, Krauthamer V, Welle CG.
  • TDT W / PI implants completely failed (W etched and PI completely flaked off) after 1 week in 87C H2O2 / PBS solution. Not surprising.
    • In the Au plated W, the Au remained, the PI flaked off, while thin fragile gold tubes were left. Interesting.
  • Pt/Ii + Parylene-C microprobes seemed to fare better; one was unaffected, others experienced a drop in impedance.
  • NeuralNexus (Si3N4 insulated, probably, plus Ir recording pads) showed no change in H2O2 RAA, strong impedance drop (thicker oxide layer?)
  • Same for blackrock / utah probe (Parylene-C), though there the parylene peeled from the Si substrate a bit.

{1275}
hide / / print
ref: -0 tags: polyimide adhesion oxygen nitrogen plasma surface energy date: 03-10-2014 22:33 gmt revision:0 [head]

Adhesion Properties of Electroless-Plated Cu Layers on Polyimide Treated by Inductively Coupled Plasmas

  • O2 then N2/H2 ICP treatment of polyimide surfaces dramatically lowers the surface energy (as measured by contact angle), and increases the adhesion of palladium-catalyzed electroless copper.
  • Particularly, C-N bonds are increased as revealed by XPS.
  • No peel-strength measurements given.